Reliable ER307 SAW Wire: Advanced Quality for Metal Joining

• Customization: Available
• Type: Rolling Wire
• Material: CO2
• Model NO.: ER307
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: <10mm
• Transport Package: 1kg/5kg/12.5/15kg/Spool
• Specification: 0.6/0.8/1.0/1.2/1.6/2.0/3.2/4.0mm
• Trademark: Jiuzhou
• Origin: China
• HS Code: 7223000
• Production Capacity: 200000kg/Year

Product Description

ER 307

Stainless steel continuous & cut length solid welding wire for MIG/TIG welding

CLASSIFICATION :TAWS/SFA-5.9: ER307 (Nr.), BS 18.8Mn
DIN 8556: WK. 1.4370
CHARACTERISTICS : ER307 is an expertly crafted Manganese-austenitic stainless steel grade, meticulously engineered to meet the demands of applications that require unparalleled toughness and exceptional crack resistance. This superior wire is ideal for MIG, TIG, and SAW welding processes. Its elevated silicon content is specifically designed to enhance weld flow, facilitating optimal weldability and producing seamless, incredibly smooth weld beads.
APPLICATION : ER 307 stands as the distinguished choice for welding in challenging environments, particularly for cladding hardenable steels, armor plates, and austenitic stainless. Additionally, it is perfectly suited for manganese wear steels and heat-resisting steels up to 850°C. This remarkable grade excels in hard-facing applications, particularly for hot work steel, stainless valve steel, and carbon steel components, offering unrivaled abrasion resistance and superior corrosion protection.
SHIELDING GAS : For achieving optimal welding outcomes, utilize either 100% Argon gas or a premium blend of Argon with 2% Oxygen gas.
CHEMICAL COMPOSITION % (solid wire chemistry)

C	Mn	Si	S	P	Ni
0.20 max.	5.00-8.00	0.30-0.65	0.030 Max	0.030 Max	8.00-10.00
Cr	Mo	Cu
17.00-20.00	0.50 max.	0.75 Max

CHEMICAL COMPOSITION % (solid wire chemistry

Type	Application	Chemical Composition	Mechanical Properties	Diameter(mm)	Net weight(kg)	Dia of spool(mm)	Dia(mm)
ER304	18Cr-8Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-0.45	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER304L	17Cr-8Ni	C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308	19Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308L	20Cr-9Ni	C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.8-4.5	5/12.5/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309	20Cr-13Ni	C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309L	20Cr-14Ni	C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309Lsi	20Cr-14Ni	C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10%	Mpa1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER321	16Cr-7Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% Ti0.73	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER310	24Cr-19Ni	C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0