C | Si | Mn | P | Cr |
0.015 | 0.48 | 1.85 | 0.015 | 20.5 |
S | N | Mo | Cu | Ni |
0.010 | <0.60 | 4.8 | 1.50 | 25.0 |
TENSILE STRENGTH | 78,000 PSI |
YIELD STRENGTH | 47,500 PSI |
ELONGATION IN 2" | 35% |
PROCESS | DIAMETER | VOLTAGE | AMPERAGE | GAS/FLUX | |
1/16" | 14-18 | 90-130 | 100% Ar | ||
TIG (GTAW) | 3/32" | 15-20 | 120-175 | 100% Ar | |
1/8" | 15-20 | 150-220 | 100% Ar | ||
.035" SHORT ARC | 16- 26 | 70-160 | 69%Ar-30%He-1%O2 | ||
MIG (GMAW) | .035" SPRAY ARC | 26- 31 | 150-230 | 92%Ar-8%Co2 or | |
.045" SPRAY ARC | 28-32 | 180-280 | 98%Ar-2%O2 | ||
SUB-ARC (SAW) | 3/32" | 28-30 | 275-350 | Record IN | |
1/8" | 29-32 | 350-450 | Record IN | ||
TIG | 10 lb. tube/40 lb. carton | |
MIG | 30 lb. spool |
C | Mn | Si | S | P | Ni |
0.030 max. | 1.00-2.50 | 0.30-0.65 | 0.030 Max | 0.030 Max | 12.00-14.00 |
Cr | Mo | Cu | |||
18.00-20.00 | 2.00-3.00 | 0.75 Max |
Type | Application | Chemical Composition | Mechanical Properties | Diameter(mm) | Net weight(kg) | Dia of spool(mm) |
Dia(mm) |
ER304 | 18Cr-8Ni | C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% |
Mpa 1200 | 0.08-0.45 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER304L | 17Cr-8Ni | C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER308 | 19Cr-9Ni | C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER308L | 20Cr-9Ni | C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% |
Mpa 1200 | 0.8-4.5 | 5/12.5/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER309 | 20Cr-13Ni | C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10% |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER309L | 20Cr-14Ni | C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10% |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER309Lsi | 20Cr-14Ni | C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10% |
Mpa1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER321 | 16Cr-7Ni | C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% Ti0.73 |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER347 | 16Cr-9Ni | C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10 |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER347L | 17Cr-9Ni | C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10 |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER316 | 16Cr-9Ni | C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03 |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER316L | 17Cr-9Ni | C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03 |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |
ER310 | 24Cr-19Ni | C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10% |
Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.6-1.6 TIG:1.0-5.0 |