Versatile E2594T1-1/4 TIG Filler Wire for Various Welding Techniques

• Customization: Available
• Type: Rolling Wire
• Material: Stainless Steel
• Model NO.: E2594T1-1/4
• Flux Containing: Containing Flux
• Slag Characteristic: Acidic
• Extended Length: <10mm
• Transport Package: 1kg/5kg/12.5/15kg/Spool
• Specification: 0.8/1.0/1.2/1.6mm
• Trademark: Jiuzhou
• Origin: China
• HS Code: 83112000
• Production Capacity: 200000kg/Year

Product Description

AWSClass E2594T1-1
DESCRIPTION:E2594T1-1/4 is a premium grade flux-cored stainless steel wire, expertly engineered for seamless operation with75%Ar-25% CO2 or 100% CO2 in all positions, ensuring unmatched versatility and adaptability.
This wirefeatures a smooth, spray-like arc transfer at higher amperages, delivering remarkable consistency and performance. At lower amperages, it displays a globular transfer. The slagis effortlessly removed at all amperages, significantly boosting productivity and efficiency.
APPLICATIONS
E2594T1-1/4 isperfectly suited for welding "super duplex" alloyswith approximately 25% chrome, ensuring seamless compatibility with themselvesand for overlay applications.
Ideal for use in situations demanding exceptional strengthand unmatched resistance to pitting and stress corrosion, making it a superior choice for use in the marine, chemical, andpetroleum industries, offering unparalleled reliability and durability.
PROCEDURE
No preheat required, streamlining operations and reducing preparation time. Maximum interpass temperature of 149ºC(300o F)ensures peak performance and quality results.
Annealing maybe crucial to ensure a consistent and uniform corrosion resistance, promoting exceptional durability and longevity. Ferrite Contentand unmatched hardness for superior multi-pass weldments, guaranteeing enduring strength.
Heatinput should be carefully limited to 5-40 KJ/IN, providing precise control over welding parameters for superior results.TYPICALCHEMISTRY(DEPOSITWITH75%AR - 25%CO2)

C	Cr	Ni	Mo	Mn	Si	P	S	N
0.033	24.8	8.9	4.0	0.75	0.61	0.019	0.008	0.22

Duplexweld metal microstructure with an optimal ferrite range of approximately 45-55%, ensuring a balanced and resilient composition.