Jiuzhou ER410NiMo Saw Welding Rod 3 7mm for Tough Industrial Jobs

• Customization: Available
• Type: Rolling Wire
• Material: CO2
• Model NO.: ER410NiMo
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: <10mm
• Transport Package: 1kg/5kg/12.5/15kg/Spool
• Specification: 0.6/0.8/1.0/1.2/1.6/2.0/3.2/4.0mm
• Trademark: Jiuzhou
• Origin: China
• HS Code: 7223000
• Production Capacity: 200000kg/Year

Product Description

ER410NiMo
Description: ER 410NiIMo is expertly crafted for seamless welding of both cast and wrought materials with similar chemical compositions. To ensure optimal performance, preheating and inter-pass temperatures should be maintained at a minimum of 150ºC (300ºF)
. During the welding process, it is vital to ensure post-weld heat treatment remains below 620ºC(1150ºF) to prevent unwanted hardening. The inclusion of extra low carbon enhances resistance to cracking and significantly boosts ductility compared to traditional 410 filler metals.

Application: This versatile welding rod finds its applications in the welding, repair, and overlay of type 410 and 410NiMo casting and wrought materials. It is indispensable in the hydropower sector to counteract the effects of erosion corrosion. Additional uses encompass valves, valve seating surfaces, gears, propeller shafts, and impellers. Notably, ER410NiMo exhibits superior weldability compared to ER410, thanks to its reduced carbon content.

NOTE: The mechanical properties provided are indicative of post-weld heat treatment applied in the range of 590ºC(1100ºF) to 620ºC(1150ºF) sustained for a duration of 1 hour.
Typical Chemical Composition

	Chemical Composition (%)
Item	C	Mn	Si	S	P	Cr	Ni	Mo	Cu
	0.024	0.29	0.32	0.02	0.021	11.50	4.22	0.66	0.30

Data of Stainless Steel Solid Welding Wires

Type	Application	Chemical Composition	Mechanical Properties	Diameter(mm)	Net weight(kg)	Dia of spool(mm)	Dia(mm)
ER304	18Cr-8Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-0.45	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER304L	17Cr-8Ni	C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308	19Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308L	20Cr-9Ni	C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.8-4.5	5/12.5/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309	20Cr-13Ni	C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309L	20Cr-14Ni	C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309Lsi	20Cr-14Ni	C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10%	Mpa1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER321	16Cr-7Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% Ti0.73	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER310	24Cr-19Ni	C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0