Advanced ER307 Welding Electrode: High-Quality for Welding Tasks

• Customization: Available
• Type: Rolling Wire
• Material: CO2
• Model NO.: ER307
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: <10mm
• Transport Package: 1kg/5kg/12.5/15kg/Spool
• Specification: 0.6/0.8/1.0/1.2/1.6/2.0/3.2/4.0mm
• Trademark: Jiuzhou
• Origin: China
• HS Code: 7223000
• Production Capacity: 200000kg/Year

Product Description

Product Code: ER 307

Introducing our Stainless Steel Continuous & Cut Length Solid Welding Wire - the ideal choice for MIG/TIG welding, where precision and strength meet seamless welds.

CLASSIFICATION DETAILS:Classification Code: TMeets Standards: AWS/SFA-5.9: ER307 (Nr.), BS 18.8Mn
Conforms to DIN 8556: WK. 1.4370
KEY CHARACTERISTICS: ER307 is a premium Manganese-austenitic stainless steel grade, expertly crafted for situations demanding superior toughness and outstanding crack resistance. Ideal for MIG, TIG, and SAW welding processes, its elevated silicon content ensures enhanced weld flow, facilitating optimal weldability and producing extraordinarily smooth weld beads.
APPLICATIONS: ER 307 is the ultimate solution for welding tasks in environments necessitating cladding on hardenable steels, armor plates, austenitic stainless, manganese wear steels, and heat-resistant steels up to 850°C. This grade is particularly outstanding in hard-facing applications for hot work steel, stainless valve steel, and carbon steel components requiring exceptional abrasion resistance and corrosion protection.
OPTIMAL SHIELDING GAS: For superior welding outcomes, use either 100% Argon gas or an Argon blend with 2% Oxygen gas.
CHEMICAL COMPOSITION % (Solid Wire Chemistry):

C	Mn	Si	S	P	Ni
0.20 max.	5.00-8.00	0.30-0.65	0.030 Max	0.030 Max	8.00-10.00
Cr	Mo	Cu
17.00-20.00	0.50 max.	0.75 Max

Detailed CHEMICAL COMPOSITION % (Solid Wire Chemistry):

Type	Application	Chemical Composition	Mechanical Properties	Diameter(mm)	Net weight(kg)	Dia of spool(mm)	Dia(mm)
ER304	18Cr-8Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-0.45	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER304L	17Cr-8Ni	C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308	19Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308L	20Cr-9Ni	C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.8-4.5	5/12.5/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309	20Cr-13Ni	C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309L	20Cr-14Ni	C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309Lsi	20Cr-14Ni	C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10%	Mpa1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER321	16Cr-7Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% Ti0.73	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER310	24Cr-19Ni	C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0