High-Quality ER347 MIG Wire: Exceptional Choice for Welding Professionals

• Customization: Available
• Type: Rolling Wire
• Material: CO2
• Model NO.: ER347
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: >20mm
• Transport Package: 1kg/5kg/12.5/15kg/Spool
• Specification: 0.6/0.8/1.0/1.2/1.6/2.0/3.2/4.0mm
• Trademark: Jiuzhou
• Origin: China
• HS Code: 7223000
• Production Capacity: 200000kg/Year

Product Description

ER 347

Discover the pinnacle of precision in welding with our stainless steel continuous & cut length solid welding wire, meticulously crafted for the ultimate performance in MIG/TIG applications.
CLASSIFICATION : AWS/SFA-5.9: ER347, BS 19.9Nb
DIN 8556: WK. 1.4551
CHARACTERISTICS : Unleash outstanding weld aesthetics with ER347 Niobium-stabilized 18Cr-8Ni type welding wires. These wires are expertly crafted to work in harmony with Argon+O2 or CO2 shielding gas mixtures, ensuring flawless results every time.
APPLICATION : Designed for excellence, ER 347's Niobium-stabilized wires are engineered for premier MIG/TIG/SA welding of AISI 321 and 18/8 types. Ideal for environments with temperatures ranging from 400°C to 850°C, its enhanced Silicon content guarantees superior weld flow and incredibly smooth weld beads.
SHIELDING GAS : Achieve optimum welding results with our expertly designed wire, facilitating seamless operations with 100% Ar gas or Ar+2%O2 gas.

Type	Application	Chemical Composition	Mechanical Properties	Diameter(mm)	Net weight(kg)	Dia of spool(mm)	Dia(mm)
ER304	18Cr-8Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-0.45	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER304L	17Cr-8Ni	C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308	19Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308L	20Cr-9Ni	C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.8-4.5	5/12.5/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309	20Cr-13Ni	C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309L	20Cr-14Ni	C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309Lsi	20Cr-14Ni	C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10%	Mpa1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER321	16Cr-7Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% Ti0.73	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER310	24Cr-19Ni	C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0