ER309L Stainless Steel Solid Welding Wire for Versatile Applications

• Customization: Available
• Type: Rolling Wire
• Material: CO2
• Model NO.: ER309L
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: <10mm
• Transport Package: 1kg/5kg/12.5/15kg/Spool
• Specification: 0.6/0.8/1.0/1.2/1.6/2.0/3.2/4.0mm
• Trademark: Jiuzhou
• Origin: China
• HS Code: 7223000
• Production Capacity: 200000kg/Year

Product Description

ER 309L

CLASSIFICATION : AWS/SFA-5.9: ER309L
CHARACTERISTICS: ER309L is austenitic Stainless steel welding wire, the weld metal contains ferrite and resistance to crack is extremely good. Due to its high level of alloy, it has excellent resistance to heat.
APPLICATION : ER 309L welding wire of  22%Cr-12%Ni steel for joining ferrite to austenite stainless steel for services temperature up o 300°C . Heat resistance cast steel clad side of 18% Cr-8% Ni clad steel and stainless steel to Cr-Mo steel or carbon steel.    
SHIELDING GAS: welding with 100% Ar gas Or Ar+2%O2 gas.    
CHEMICAL COMPOSITION % ( solid wire chemistry )

C	Mn	Si	S	P	Ni
0.030 max.	1.00-2.50	0.30-0.65	0.030 Max	0.030 Max	11.00-14.00
Cr	Mo	Cu
22.00-26.00	0.75 max.	0.75 Max

Data of  Stainless Steel Solid Welding Wires

Type	Application	Chemical Composition	Mechanical Properties	Diameter(mm)	Net weight(kg)	Dia of spool(mm)	Dia(mm)
ER304	18Cr-8Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-0.45	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER304L	17Cr-8Ni	C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308	19Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308L	20Cr-9Ni	C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.8-4.5	5/12.5/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309	20Cr-13Ni	C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309L	20Cr-14Ni	C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309Lsi	20Cr-14Ni	C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10%	Mpa1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER321	16Cr-7Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% Ti0.73	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER310	24Cr-19Ni	C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0