Efficient ER309L Solid Welding Wire for Industrial Applications

• Customization: Available
• Type: Rolling Wire
• Material: CO2
• Model NO.: ER309L
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: <10mm
• Transport Package: 1kg/5kg/12.5/15kg/Spool
• Specification: 0.6/0.8/1.0/1.2/1.6/2.0/3.2/4.0mm
• Trademark: Jiuzhou
• Origin: China
• HS Code: 7223000
• Production Capacity: 200000kg/Year

Product Description

ER 309L

CLASSIFICATION :AWS/SFA-5.9: ER309L
CHARACTERISTICS: ER309L is a superior quality austenitic stainless steel welding wire. It is renowned for its exceptional ability to resist cracking, thanks to the ferrite in the weld metal. Its high alloy composition ensures it excels in withstanding heat, making it ideal for demanding industrial applications.
APPLICATION :This versatile ER309L welding wire is expertly crafted for joining 22%Cr-12%Ni steel, particularly adept at connecting ferrite to austenite stainless steel for use in environments up to 300°C. It is perfect for heat-resistant cast steel clad sides of 18% Cr-8% Ni clad steel, as well as for joining stainless steel to Cr-Mo steel or carbon steel.
SHIELDING GAS: For optimal performance, utilize welding with 100% Argon gas or a mix of Argon with 2% Oxygen gas.
CHEMICAL COMPOSITION % (solid wire chemistry)

C	Mn	Si	S	P	Ni
0.030 max.	1.00-2.50	0.30-0.65	0.030 Max	0.030 Max	11.00-14.00
Cr	Mo	Cu
22.00-26.00	0.75 max.	0.75 Max

Data on Stainless Steel Solid Welding Wires

Type	Application	Chemical Composition	Mechanical Properties	Diameter(mm)	Net weight(kg)	Dia of spool(mm)	Dia(mm)
ER304	18Cr-8Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-0.45	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER304L	17Cr-8Ni	C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308	19Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER308L	20Cr-9Ni	C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10%	Mpa 1200	0.8-4.5	5/12.5/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309	20Cr-13Ni	C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309L	20Cr-14Ni	C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER309Lsi	20Cr-14Ni	C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10%	Mpa1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER321	16Cr-7Ni	C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% Ti0.73	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER347L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% (Ta+Nb)(10*C)-10	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316	16Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER316L	17Cr-9Ni	C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0
ER310	24Cr-19Ni	C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10%	Mpa 1200	0.08-4.5	5/10/15/20	100/270/300	MIG:0.6-1.6 TIG:1.0-5.0